Alloy 8020 Nickel / Chromium UNS N06003lpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

Download Datasheet

Strip, Coil, Foil & Wire lpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

Applications lpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

Electrical heating elements for industrial devices such as flat irons, water heaters, plastic moulding dies, soldering irons

Description lpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

This alloy can be used at operating temperatures up to 1200 °C , (2190 °F). Its chemical composition gives good oxidation resistance especially under conditions of frequent switching or wide temperature fluctuations.

Chemistry Typical lpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

Nickel: 80% Chromium: 20%

Physical Properties lpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

Density: 0.303 lb/in3, 8.31 g/cm3

Electrical Resistivity: ohm-cir-mil/ft ( ohm-mm2 /mm ):
At 68 ° F (20 ° C): 650 (1.08)
At 212 F (100 °C): 656 (1.09)
At 392 F (200 °C): 662 (1.10)
At 572 F (300 °C): 668 (1.11)
At 752 F (400 °C): 680 (1.13)
At 1290 F (700 °C): 686 (1.14)
At 1470 F (800 °C): 686 (1.14)
At 1650 F (900 °C): 686 (1.14)
At 1830 F (1000 °C): 692 (1.15)
At 2010 F (1100 °C): 699 (1.16)
At 2190 F (1200 °C): 704 (1.17)

Specific Heat: BTU/lb-° F (J/g-° C):
At 68 ° F (20 ° C): 0.107 (0.448)

Thermal Conductivity: BTU-in/hr-ft2-°F (W/m?K): 133 (19.2)

Mean Coefficient of Thermal Expansion: ?in/in-°F (?m/m-°C):
At 68 - 212 °F (20 - 100 °C): 6.94 (12.5)

Melting Temperature: 2550 °F (1400 °C)

Forms lpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

Coil - Sheet, Strip, Foil Wire - Profile, Round, Flat, Square

Mechanical Properties at Room Temperature lpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

Properties: Annealed Typical lpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

Ultimate Tensile Strength: 95000 KSI (655 MPa)

Properties: Temperedlpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

Alloy 80/20 can be cold worked to various tempers. Contact Ulbrich Technical Service for additional information.

Additional Propertieslpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

Corrosion Resistancelpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

Refer to NACE (National Associate of Corrosion Engineers) for recommendations.

Finisheslpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

#1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required.
#2D - Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process. #2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D.
#BA- Bright annealed cold rolled and bright annealed
#CBA- Course bright annealed cold rolled matte finish and bright anneal
#2 - Cold Rolled
#2BA- Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part. Polished - Various grit finish for specific polish finished requirements.
* Not All Finishes are Available for All Alloys - Consult Sales for Applicable Finishes.

Wire Finisheslpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

XC - Extra Clean Bright Annealed or Bright Annealed and Cold Rolled Grease - Ultra bright finish (for decorative applications) Soap - Soap coating on tempered wire to act as lubricant * Contact Ulbrich Wire with special wire finishes.

Heat Treatmentlpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

Alloy 80/20 is non hardenable by heat treatment.

Weldinglpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

For best results refer to: SSINA's "Welding of Stainless Steels and Other Joining Methods".




Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels & Special Metals, Inc., be liable for any damages arising from the use of the information included in this document or that it is suitable for the 'applications' noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document.

Contact Us lpls系列比赛数据,lplS10半决赛直播,英雄联盟外围投注网站

Full Name
Email
Company
Title
City, State, Country
Phone (Optional)
Message (Optional)